1. Chemical composition
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Mo |
Other elements |
0,2 |
0,55 |
1,6 |
0,035 |
0,035 |
- |
- |
- |
|
2. mechanical properties
Condition |
Nominal thickness |
Tensile strength |
Plug-in.limit |
Ultimate elongation |
Rigor |
|
in mm |
Rm in MPa |
Rp0,2 in MPa |
in % (min.) |
HBS |
over |
over |
up to |
min |
max |
min |
max |
A50 |
A |
|
grounded |
5 |
60 |
450 |
630 |
295 |
355 |
18-22 |
- |
- |
|
General properties |
(Guide values for 20° C) |
|
Density of g/cm3 |
7,85 |
Special annealing |
- |
Thermal conductivity W/(mK |
35-45 |
Workability |
2 |
Modulus of elasticity kN/mm2 |
|
Dimensional stability |
|
Therm. linear expansion- |
|
Weldability |
4 |
Coeffizient 10-6/K |
11-14 |
Corrosion resistance |
5 |
|
|
Acid resistance |
5 |
Standard tolerances |
|
Surface treatment |
|
Surface quality Ra |
1,6 |
Hardening |
4 |
Thickness tolerance mm |
+0,3/-0 |
Nickel-plating |
2 |
Length and width tolerance mm |
-0/+2 |
|
|
Parallelism mm |
<0,1 |
|
|
Flatness mm |
<0,5 |
|
|
3. Type:
material normalized, thickness ground, length and width sawn or plasma cut
Against surcharge: Outside contour milled with tolerance of +/-0.2 mm
4. Main application / Special features:
Base plate, table plate, mounting plate, cladding plates